EN 10088-2  1.4404 Stainless Steel Plate 316L Stainless Steel Supplier in China

Grade 316L, the low carbon version of 316 and is immune from sensitization (grain boundary carbide precipitation). Thus it is extensively used in heavy gauge welded components (over about 6mm). There is commonly no appreciable price difference between 316 and 316L stainless steel.

The austenitic structure also gives these grades excellent toughness, even down to cryogenic temperatures.

Compared to chromium-nickel austenitic stainless steels, 316L stainless steel offers higher creep, stress to rupture and tensile strength at elevated temperatures.

Composition of 316L Stainless Steel

Mechanical Properties of 316L Stainless Steel

Corrosion Resistance of 316L Stainless Steel

Excellent in a range of atmospheric environments and many corrosive media - generally more resistant than 304. Subject to pitting and crevice corrosion in warm chloride environments, and to stress corrosion cracking above about 60 °C. Considered resistant to potable water with up to about 1000 mg/L chlorides at ambient temperatures, reducing to about 500 mg/L at 60 °C.

316 is usually regarded as the standard "marine grade stainless steel", but it is not resistant to warm seawater. In many marine environments, 316 does exhibit surface corrosion, usually visible as brown staining. This is particularly associated with crevices and rough surface finish.

Heat Resistance of 316L Stainless Steel

Good oxidation resistance in intermittent service to 870 °C and in continuous service to 925 °C. Continuous use of 316 in the 425-860 °C range is not recommended if subsequent aqueous corrosion resistance is important. Grade 316L is more resistant to carbide precipitation and can be used in the above temperature range. Grade 316H has higher strength at elevated temperatures and is sometimes used for structural and pressure-containing applications at temperatures above about 500 °C.

Heat Treatment of 316L Stainless Steel

Solution Treatment (Annealing) - Heat to 1010-1120 °C and cool rapidly. These grades cannot be hardened by thermal treatment.

Machining of 316L Stainless Steel

316L stainless steel tends to work harden if machined too quickly. For this reason, low speeds and constant feed rates are recommended.

316L stainless steel is also easier to machine compared to 316 stainless steel due to its lower carbon content.

Hot and Cold Working of 316L Stainless Steel

316L stainless steel can be hot worked using the most common hot working techniques. Optimal hot working temperatures should be in the range 1150-1260 °C, and certainly should not be less than 930 °C. Post-work annealing should be carried out to induce maximum corrosion resistance.

Most common cold working operations such as shearing, drawing, and stamping can be performed on 316L stainless steel. Post-work annealing should be carried out to remove internal stresses.

Applications of 316L Stainless Steel

Typical applications include:

• Food preparation equipment particularly in chloride environments.
• Pharmaceuticals
• Marine applications
• Architectural applications
• Medical implants, including pins, screws and orthopedic implants like total hip and knee replacements
• Fasteners