Wear Resistant Protective Coating, Anti Abrasion Protective Coating, Wear Compound

Model NO.
TS11490F
Material
Epoxy
Classification
Room Curing
Main Agent Composition
Epoxy Resin
Characteristic
Waterproof
Promoter Composition
Curing Agent
Composition
Organic Material
Color
Grey
Certificate
MSDS, TDS
Shelf Life
1 Year
OEM Service
Yes
Free Sample
Yes, Buyer Need Pay Freight
Transport Package
10kg/Drum
Specification
10kg/set, 20kg/set
Trademark
Customized
Origin
China
HS Code
3214109000
Production Capacity
30000tons/Month
Reference Price
$ 13.50 - 14.40
Contact Us

Product Description

TS11490F 8 hours curing  ceramic bead filled epoxy wear compound, anti-abrasion protective coating

Wear Resistant Protective Coating, Anti Abrasion Protective Coating, Wear Compound Wear Resistant Protective Coating, Anti Abrasion Protective Coating, Wear Compound

Product Description:

High-density, alumina ceramic bead-filled, toughened epoxy system for repairing and protecting equipment from wear and abrasion caused by handling and processing particulate matter as solid or in slurry form.

Product Features:
 

1. ceramic-filled for outstanding resistance to abrasion

2. Renews worn surfaces fast-reduces downtime

3. Extends wear life- resists sliding abrasive wear and eliminates costly wear part inventory

4. Non sag- provides abrasion resistance on over-head and vertical surfaces.



Product Application:

1. Cyclone and separator bodies

2. Dust collectors and exhausters

3. Pump liners and impellers

4. Fan blades and housings

5. Chutes and hoppers

6. Elbows and transition points

Wear Resistant Protective Coating, Anti Abrasion Protective Coating, Wear Compound


Technical Data:
 

Color:

Grey              

Specific gravity:

2.43g/cm³

Mix ratio by weight:

8:1

Mix ratio by volume:

4:1

Working time(min):

65min

Compressive strength(GB/T1041): 112.0MPa
Tensile strength(GB/T6329): 32.0MPa
Shear strength(GB/T7124): 14.0MPa
Flexural strength(GB/T9341): 45.0MPa

Fully cured time:

24h

Temperature range:

-60~160ºC



How to Use:

1. Surface treatment :
roughening the parts to be treated, sanding or sandblasting with an angle grinder, etc.; cleaning the roughened surface; the treated surface should be a rough and dry fresh substrate surface, and should be No oil and dust.
2. Preparation :
Mix the components A and B of the small particle wear-resistant protective agent according to the mass ratio A:B=4:1, and use them within 30 minutes.
3. Coating :
apply the uniformly mixed small particles of wear-resistant protective agent layer by layer to the area to be repaired, preferably at a thickness of 3-10 mm. The adhesive layer should be compacted to fully infiltrate the substrate; after the coating is applied to the required size, the surface layer is smoothed.
4. Curing :
Curing at 25ºC for 16 hours can be put into use. When the temperature is lower than 10 degrees, it can be cured by baking with an iodine tungsten lamp or electric heating plate for 2 hours.


Packing:

500g/set,  10kg/set 


Transport and storage:

Keep the epoxy coating in dry, cool and covered facility, shelf life is 1 year. Avoid inversion and collision in transportation. This product is not dangerous goods.


 

 

Adhesive