High Wear Resistance Raised Ceramic Mosaic Tile Vulcanized in Pulley Lagging

Model NO.
ceramic mosaic tile
Raw Material
Alumina Powder
Size
Customized
Shape Way
Plain,Weldable,Curved,Trapezoidal,Dimple
Character
High Purity/Hardness, Abrasion-Resistant
Color
White
Firing Temperature
1550~1680degree Centigrade
Apparent Porosity
0
OEM
Accept
Transport Package
Paper Carton+Pallet
Specification
20*20, 31*31, 40*40, 35*35
Trademark
Chemshun
Origin
Pingxiang, China
HS Code
69091900
Production Capacity
50000ton/Year
Reference Price
$ 899.10 - 1,799.10
Contact Us

Product Description

High Wear Resistance Raised Ceramic Mosaic Tile Vulcanized in Pulley Lagging

Product Description
With the characteristics of easy construction . ceramic liners are broadly applied on transfer points of a conveyor, they are not only suitable for chutes,feeding pipes, elbow and straight pipes, but also for emergency maintenance such as the repairs of performation on rubber and the sheel of pulleys .raised ceramic mosaic tile are designed to increase the coefficient of friction between the lagging and the belt . they will provide a longer service life for the pulley and belt. while enabling the system to run at a lower tension, reducing power consumption 

Alumina ceramic cylinder characters
--  High hardness with Moh's hardness 9 grade 
--  High abrasion and chemical resistance 
--  Special dumps designed for more wear resistance 
--  Light weight with various sizes 

Sizes
Ceramic lining pieces size   
17.5*17.5*5mm    19.95*19.95*4.5*0.6 with dimples
17.5*17.5*4mm    20*30*5 with 18 pieces dimples
17.5*17.5*3mm      20*20*4 with 13 pieces dimples
20*20*4/5/6mm  20*20*8mm with 8 pieces dimples 
20820*12/13mm   
25*25*4mm  
Note: more customized size available   

Tenical Data Sheet
Specific gravity (g/cc) >3.60
Apparent porosity (%) 0
Flexural Strength (20ºC, Mpa) 270
Compressive strength (20ºC, Mpa) 850
Rockwell hardness (HRA) 80
Vickers hardness (hv) 1000
Moh ' s hardness (scale) ≥9
Thermal Expansion (20-800ºC, x10-6/ºC) 8
Crystal Size (μm) 1.3~3.0
Fracture Toughness (Mpa.M 1/2 ) 3-4
Maximum Operation Temperature(ºC) 1450

High Wear Resistance Raised Ceramic Mosaic Tile Vulcanized in Pulley Lagging
High Wear Resistance Raised Ceramic Mosaic Tile Vulcanized in Pulley Lagging
High Wear Resistance Raised Ceramic Mosaic Tile Vulcanized in Pulley Lagging
High Wear Resistance Raised Ceramic Mosaic Tile Vulcanized in Pulley Lagging
High Wear Resistance Raised Ceramic Mosaic Tile Vulcanized in Pulley Lagging
High Wear Resistance Raised Ceramic Mosaic Tile Vulcanized in Pulley Lagging

 

 

Anticorrosive Material