GH2136 nickel-based superalloy is a Fe-Ni-Cr-based precipitation hardening deformation superalloy, and its service temperature is below 700ºC.

Chemical Composition %
Carbon                 ≤  0.06
Chromium        13.0 - 16.0
Mo lybdenum        1.00-1.75
Nickel                24.5 - 28.5
Tungsten                  -
Aluminum              ≤  0.35
Niobium                    -
Titanium              2.40-3.20
Iron                      Balance
Silicon                ≤   0.75
Manganese          ≤  0.35
Phosphorus      ≤   0.025
Sulfur                ≤    0.025
Boron              0.005-0.025
V anadium            0.01-0.10

Physical properties:

Density:  8.03g/cm3