300mL/cartridge 500mL/sausage

450g/cartridge  750g/ sausage

One-part, neutral cure, non-corrosive to metal, coated glass, marble, etc.

Good extrusion, easy to use

Releasing low-molecular-weight alcohol and no unpleasant odor during curing

Excellent resistance to weather, UV, ozone, water

Excellent adhesive strength to lots of construction materials

Good compatibility with other neutral silicone sealants

Excellent performance at -50ºC ~150ºC after curing

Specially designed for sealing in all type door, window and wall joints

Interior decoration sealing.

Sealing for other general purposes

ACE-172 should not be applied:

To building materials that bleed oil, plasticized or solvent, to materials such as impregnated wood, oil-based caulks, green or partially vulcanized rubber gaskets, or tapes or bituminous below-grade waterproof and asphalt-impregnated fiberboard.

In totally confined spaces.

When substrate surface temperature is over 45 ºC or below-5 ºC.

Primer is not usually required when using ACE-172. However, sealant adhesion should always be tested in advance to determine the need of a primer or not. If required, the primer should be applied into a thin film to the joint surface by using a clean lint-free cloth and allowed to dry before sealant application

ACE-172 begins curing when it contacts with the moisture in air. It generally cures 2mm/day, and takes 21 days for fully-cure. In the beginning of using the sealant, please remain the sealant places fixed and flat. Solvent can be used to clean the fractured sealants and then fill up with the new sealants with same color and quality.

It is nontoxic after entirely cured. Avoid direct contact with eyes when operating. If happened, rinse opened eye under running water for several minutes. During the curing process, sealant will release a small amount of organic molecules. Construction should ensure good ventilation. If necessary, take protective measures.

Please keep children out of reach.

Technical Data

Density

1.5 g/cm3 

Slump

Elastic recovery

91%

Tensile modulus

0.7MPa

Loss of Mass

3.5%

VOC

32g/L