Chemical Composition:
al
Al(min):
99%-99.9%
Weight:
20/25kg,1000kg/case
Appearance:
silvery white
Aluminum ingot:
Aluminum ingot for remelting:
--15kg, 20kg(≤99.80%Al)
T-shaped aluminum ingot:
--500kg, 1000kg (≤99.80%Al)
High-purity aluminum ingot:
--l0kg, 15kg (99.90%~99.999%Al)
Aluminum alloy ingot:
--10kg, 15kg (Al--Si, Al--Cu, Al--Mg)
Plate ingot:
--500~1000kg (for plate making)
Round ingot:
--30~60kg (for wire drawing)
Grade: 8 series, 1100 1050 2024 2023 3003 5052 6061 6063 7075 7021 etc
Shape: brick-shaped
Size: 800*180*90mm or as required
Surface: Mill finish, polished, anodized, electrophoretic coated, powder spray coated, fluorocarbon powder spray coated /PVDF paint, draw bench, steel polished, wood grain coated /wooden transfer
Temper: T3, T4, T6, T7, T351, T451, T651, T851
Hardness: as per customer's actual request
Equipment: CNC, extruding machine, cold drawn machine, heating oven, straightening machine, cutting machine
Package: Standard export package or as required
The main models: AL99.90, AL99.85, AL99.70A, AL99.70, AL99.60, AL99.50, AL99.00
1. mainly used for melting ingot;
2. discontinuous melting with scrap ;
3. easy control and operation ;
4. fast melting;
5. Used for industry such as automobile,pinning and weaving,electron broadly and so on.
Packing:
Standard Export Package,
Metal belt, wooden plate or as customer's requests.
Aluminum ingot for remelting is produced by molten salt electrolysis method using alumina and cryolite. Products meet the national standard GB/T1196-2002. The surface of ingot is clean and smooth.
Applications:
1. mainly used for melting ingot
2. discontinuous melting with scrap
3. easy control and operation
4. fast melting
5. Used for industry such as automobile,pinning and weaving,electron broadly and so on
The main models are as follows: AL99.90, AL99.85, AL99.70A, AL99.70, AL99.60, AL99.50, AL99.00