Ualloy104B
(Common Name:Ni30Cr20,Nikrothal 30, N3, HAI-NiCr 30, Resistohm 30,30-20 Ni-Cr,Nikrothal 3.)
Ualloy104B is a nickel-chromium alloy (NiCr alloy) characterized by High resistivity, good oxidation resistance,very good form stability,good ductility and excellent weldability. It is suitable for use at temperatures up to 1100 ° C.
Typical applications for Ualloy104B are used in olid hot plates,open coil heaters in HVAC systems,night-storage heaters,convection heaters,heavy duty rheostats and fan heaters. And also used for heating cables and rope heaters in defrosting and de-icing elements,electric blankets and pads, car seats,baseboard heaters,floor heaters and resistors.
Normal composition%
|
C |
P |
S |
Mn |
Si |
Cr |
Ni |
Al |
Fe |
Other |
|
Max |
|||||||||
|
0.08 |
0.02 |
0.015 |
1.00 |
1.0~2.0 |
18.0~21.0 |
30.0~34.0 |
- |
Bal. |
- |
Typical Mechanical properties 1.0mm
|
Yield strength |
Tensile Strength |
Elongation |
|
Mpa |
Mpa |
% |
|
340 |
675 |
35 |
Typical Physical properties
|
Density (g/cm3) |
7.9 |
|
Electrical resistivity at 2 0 ºC ( mm2/m) |
1.04 |
|
Conductivity coefficient at 20 ºC (WmK) |
13 |
|
Coefficient of thermal expansion |
|
|
Temperature |
Coefficient of Thermal Expansion x10-6/ ºC |
|
20 ºC - 1000 ºC |
19 |
|
Specific heat capacity |
|
|
Temperature |
20 ºC |
|
J/gK |
0.50 |
|
Melting point ( ºC ) |
1390 |
|
Max continuous operating temperature in air ( ºC ) |
1100 |
|
Magnetic properties |
non-magnetic |
Temperature Factors Of Electrical Resistivity
|
20 ºC |
100 ºC |
200 ºC |
300 ºC |
400 ºC |
500 ºC |
600 ºC |
|
1 |
1.023 |
1.052 |
1.079 |
1.103 |
1.125 |
1.141 |
|
700 ºC |
800 ºC |
900 ºC |
1000 ºC |
1100 ºC |
1200 ºC |
1300 ºC |
|
1.158 |
1.173 |
1.187 |
1.201 |
1.214 |
1.226 |
- |
Style of supply
|
Alloys Name |
Type |
Dimension |
|
|
|
Ualloy104BW |
Wire |
D=0.03mm~8mm |
|
|
|
Ualloy104BR |
Ribbon |
W=0.4~40 |
T=0.03~2.9mm |
|
|
Ualloy104BS |
Strip |
W=8~250mm |
T=0.1~3.0 |
|
|
Ualloy104BF |
Foil |
W=6~120mm |
T=0.003~0.1 |
|
|
Ualloy104BB |
Bar |
Dia=8~100mm |
L=50~1000 |
|