Nas630 S17400 Stainless Steel Shaft Stock Precipitation Hardened Microstructure

Model NO.
NAS630
Surface Treatment
Bright
Transport Package
Export Standard Package, Bundled or Be Required.
Specification
Diameter 0.1~500mm
Trademark
ABOOM
Origin
China
HS Code
722220
Production Capacity
150000tons Per Year
Reference Price
$ 8.89 - 9.21
Contact Us

Product Description


Product Description
Item
Stainless steel bar/rod
Standard
ASTM A479,ASTM A276,ASTM A484, ASTM A582,  
ASME SA276, ASME SA484, GB/T1220, GB4226, etc.
Material
301, 304, 304L, 309S, 321, 316, 316L, 317, 317L, 310S, 201,202
321, 329, 347, 347H ,254SMO,201, 202, 410, 420, 430, S20100, S20230, S30100, S30400, S30403, S30908, S31008, S31600, S31635, etc.
Specifications
Round bar:Diameter 0.1~500mm
Angle bar:Size 0.5mm*4mm*4mm~20mm*400mm*400mm
Flat bar:Thickness 0.3~200mm        Width 1~2500mm
Square bar:Size 1mm*1mm~800mm*800mm
Length
2m, 5.8m, 6m, or as required.
Surface
Black, peeled, polishing, bright, sand blast, hair line, etc.
Price Term
Ex-work, FOB, CFR, CIF, etc.
Payment Term
A: 100% T/T advance. ( For small order<$5000.)B: 30% T/T and balance before shipping .C: 30% T/T advance, balance L/C at sight D:30% T/T , balance L/C usance E: 100% L/C usance.F: 100% L/C at sight.
Package
Export standard package, bundled or be required.
The inner size of container is below:
20ft GP: 5.9m(length) x 2.13m(width) x 2.18m(high)about 24-26CBM
40ft GP: 11.8m(length) x 2.13m(width) x 2.18m(high) about 54CBM
40ft HG: 11.8m(length) x 2.13m(width) x 2.72m(high) about 68CB


NAS630 S17400 Stainless Steel Shaft Stock Precipitation Hardened Microstructure

 

NAS630 S17400 17-4PH precipitation hardened stainless steel Shaft stock

 

The NAS630 S17400 17-4PH alloy is a precipitation, quenched, martensitic stainless steel, and this grade has high strength, hardness (up to 300 0 C / 5000 C) and corrosion resistance. After heat treatment, the mechanical properties of the product are more complete, and it can reach compressive strength of up to 1100-1300 mpa (160-190 ksi). This grade cannot be used above 300 0C (572 0F) or very low temperature. It has good corrosion resistance to the atmosphere and diluted acids or salts. It has the same corrosion resistance as 304 and 430.

 

3/16"

1/4"

5/16"

3/8"

7/16"

1/2"

9/16"

5/8"

3/4"

7/8"

1"

4.8mm

6.3mm

7.9mm

9.5mm

11.1mm

12.7mm

14.3mm

15.9mm

19mm

22.2mm

25.4mm

 

1 1/8"

1 1/4"

1 1/2"

1 3/4"

2"

2 1/4"

2 1/2"

2 3/4"

3"

3 1/2"

4"

28.6mm

31.8mm

38.1mm

44.5mm

50.8mm

57.2mm

63.5mm

69.9mm

76.2mm

88.9mm

101.6mm

 

Application area:
Offshore platforms, helicopter decks, other platforms
food industry
Pulp and paper industry
Aerospace (turbine blades)
mechanical part
Nuclear waste barrel

 

 

chemical composition:

C

Cr

Ni

Cu

Nb/Cb

Mn

0.04

16.5

4.5

3.3

0.3

0.7

PREN (%Cr+3.3%Mo+16%N)≥17

Mechanical properties

Hardened

YS 0.2%
N/mm

UTS
N/mm

Min.

Typ.

Min.

Typ.

A

1070

1207

1170

1310

B

790

931

965

1034

Hardened

YS 0.2%
ksi

UTS
ksi

 

El%

Min.

Typ.

Min.

Typ.

 

Min.

Typ.

A

155

175

170

190

 

8

14

B

115

135

140

150

 

10

17

Hardened at 496 ° C (925 ° F)-4 hours-air cooled
Hardened 593 ° C (1100 ° F)-4 hours-air cooled
The above are two examples of heat treatment.

NAS630 S17400 17-4PH precipitation hardened stainless steel Shaft

Nas630 S17400 Stainless Steel Shaft Stock Precipitation Hardened Microstructure

Hardness/Temperature tempered for 4 hours after austenitizing at 1040°C (1904°F) for 30 min quenched 100°C/sec (212°F/sec).

 

Nas630 S17400 Stainless Steel Shaft Stock Precipitation Hardened Microstructure Nas630 S17400 Stainless Steel Shaft Stock Precipitation Hardened Microstructure Nas630 S17400 Stainless Steel Shaft Stock Precipitation Hardened Microstructure

 