ASTM 310S Stainless Steel Round Bar with High Quality

Model NO.
310S
Surface Treatment
Grinded, Peeled, Polished, Rough Turned
Similar Grades
Uns S31008
Size Range
Diameter: 20-480mm
Delivery Condition
Annealed, Qunched and Tempered
Surface Condition
Grinded, Peeled, Polished, Rough Turned
Quality Standard
ASTM-A276
Transport Package
Apply The Shipping Packing
Specification
Diameter: 20-480mm
Trademark
CHENGQUAN
Origin
Hubei, Huangshi
HS Code
7228600000
Production Capacity
500tons Per Month
Reference Price
$ 450.00 - 4,500.00
Contact Us

Product Description


Similar Grades:
 UNS S31008
Shape: 
Round, Flat, Square.
Size Range:
 
Diameter(mm) 		Thickness (mm) Width (mm) Length(mm)
Round 20-480 - - 2000-5800
Square 20-480 - - 2000-5800
flat - 20-50 80-600 2000-5800

 
Steel-making Condition: 
EF, EF/EAF+LF+VD, EF/EAF+ESR
Delivery Condition:
Annealed , Quenched + Tempered

Surface Condition: 
Black, Grinded, Peeled, Rough turned, Polished

Features:

2.Immediate delivery
3.Premium quality
4.Reliable service
5.MOQ: 1 Ton
 

Packing details 		In seaworthy packing, as your requirement.
Delivery details within 30-50 days

 
Chemical Composition:

C 		Mn P S Si Cr Ni N
0.08max 2.00max 0.045max 0.030max 1.5max 24.0-26.0 19.0-22.0 /

 
 
Mechanical Properties
The following table outlines the mechanical properties of grade 310S stainless steel.

Properties 		Metric Imperial
Tensile strength 515 MPa 74695 psi
Yield strength 205 MPa 29733 psi
Elastic modulus 190-210 GPa 27557-30458 ksi
Poisson's ratio 0.27-0.30 0.27-0.30
Elongation 40% 40%
Reduction of area 50% 50%
Hardness 95 95

 
 
Fabrication and Heat Treatment
Machinability
Grade 310S stainless steel can be machined similar to that of grade 304 stainless steel.
Welding
Grade 310S stainless steel can be welded using fusion or resistance welding techniques. Oxyacetylene welding method is not preferred for welding this alloy.
Hot Working
Grade 310S stainless steel can be hot worked after heating at 1177C (2150F). It should not be forged below 982C (1800F). It is rapidly cooled to increase the corrosion resistance.
Cold Working
Grade 310S stainless steel can be headed, upset, drawn, and stamped even though it has high work hardening rate. Annealing is performed after cold working in order to reduce internal stress.
Annealing
Grade 310S stainless steel is annealed at 1038-1121C (1900-2050F) followed by quenching in water.
Hardening
Grade 310S stainless steel does not react to heat treatment. Strength and hardness of this alloy can be increased by cold working.
Applications
Grade 310S stainless steel is used in the following applications:
· Boiler baffles
· Furnace components
· Oven linings
· Fire box sheets
· Other high temperature containers.
 