Centrifugal Casting Cual

HS Code
8454909000
Reference Price
Please contact us for quote
Contact Us

Product Description

This product is made by changing the heat treatment method of the alloy with special dual-phase structure and precise control of each production link. It has higher ultimate strength, yield strength and hardness
Mechanical and physical  Units
Nominal value
Tensile strength R m MPa  793
Specified non-proportional extension strength R p 0.5 MPa  407

Elongation after breaking A 		% 10

Brinell hardness 		HBW 10/3000 228

Rockwell hardness 		HRB 98

Reduction of area Z 		% 8

Compressive strength R mc 		Mpa 1069

Specified non-proportional compressive strength R pc 0.1 		Mpa 441

Compression ratio limit R pc 		Mpa 338

Shear strength R cm 		Mpa 427

Elastic modulus E 		Gpa 110

Charpy shock absorption energy AK 		J 11

Izod impact absorption power AK 		J 16.3
Fatigue strength (100'000'000 times) σN Mpa 248

Density ρ 		g / cm³ 7.45

Coefficient of linear expansion α 		10 -6 / K 16.2

Thermal conductivity λ 		W / m · K 59

Conductivity γ 		m /  Ω· mm² 7.5

Conductivity 		% I.A.C.S. 13

Specific heat capacity cp 		J / g · K 0.42

Application:
This product can meet the strict requirements of the aircraft industry. It has higher physical properties, hardness and sufficient ductility to withstand extreme shocks and loads. It is recommended to be used as bushes, bearing bushes, gaskets, inserts, piston parts, nuts and sliders.
Chemical composition
Al:10.5%   Fe:3.5%  Other:Up to 0.5%    The rest is copper Centrifugal Casting Cual Centrifugal Casting Cual Centrifugal Casting Cual Centrifugal Casting Cual Centrifugal Casting Cual Centrifugal Casting Cual
 

 

Alloy