Test Parameter | Unit | Result |
As Supplied Tested at 23ºC and 50% RH | ||
Specific Gravity | g/ml | 0.9 4 ±0.02 |
Flow (sag or slump) | mm | 0 |
Extrusion Rate | ml/minute | 130 |
Skin Time | minute | 5~10 |
Tack-free Time | hour | ≤1.0 |
Curing time (5mm) | hour | ≤18 |
As Cured-after 21 days at 23ºC and 50% RH | ||
Durometer Hardness, Shore A | Points | 18 |
Movement Capability | % | ±20 |
Tensile/Modulus at 50% Elongation | Mpa | 0.28 |
Tensile/Modulus at 100% Elongation | Mpa | 0.3 |
Ultimate Tensile Strength
Ultimate Elongation at Break |
Mpa
% |
0.4
375 |