Heat Curable Epoxy Based High Performance Impact Resistant Structural Adhesive Replace Teroson Ep 5016

Model NO.
TS5016
Material
Epoxy
Classification
Room Curing
Main Agent Composition
Epoxy Resin
Characteristic
Waterproof
Promoter Composition
Curing Agent
Composition
Epoxy
Color
Black
Transport Package
Paper Carton
Specification
450g/tube
Trademark
Customized
Origin
China
HS Code
3506100010
Production Capacity
500000PCS/Month
Reference Price
$ 6.30 - 58.50
Contact Us

Product Description

TS-5016 is heat cure epoxy caulking adhesive for powder coating. It's the replacement of Teroson EP 5016.

Heat Curable Epoxy Based High Performance Impact Resistant Structural Adhesive Replace Teroson Ep 5016 Heat Curable Epoxy Based High Performance Impact Resistant Structural Adhesive Replace Teroson Ep 5016


Substrate Type:
Hot dip Galvanized Steel, Electro Galvanized Steel, Galvannealed Steel, Cold Rolled Steel.


Heat Curable Epoxy Based High Performance Impact Resistant Structural Adhesive Replace Teroson Ep 5016


Product Application:
It is used in the body shop of metal bonding. TS5016 provides improved impact resistance, stiffness, and durability in the structure.

Heat Curable Epoxy Based High Performance Impact Resistant Structural Adhesive Replace Teroson Ep 5016


Curing Method:
Heat curable. Normally, heating temperature is 190ºC, and curing time is 30 minutes. It can resist 223ºC for some hours in oven.


Product Technology:
TS5016 is a heat curing, solvent free, metal to metal adhesive with good storage stability based on epoxy resins. The meterial can be spot-welded through and will reach maximum strength with curing temperature between 155ºC to 200ºC. The product exhibits excellent strength and corrosion and resistance at temperature extremes or after extensive aging and weathering. It provides exceptional impact resistance over a wide temperature range.

Technical Data Sheet:
 
Colo White
Odor None
Appearance Consistency Paste
Solids ≥99%
Specific Gravity ≤1.2
Lab Shear Strength @ 23ºC ≥25MPa
T-Peel @ 23ºC ≥250N/25mm
Viscosity 40mm parallel plate, 50ºC, shear rate 1/s 30-50 Pa.s
Impact Peel Resistance @ 23ºC ISO 11343(2m/s), 1.6mm CRS
Bake 15 minutes @ 155ºC ≥35N/mm
Shear Strength @ 23ºC 1.6mm CRS
Bake 15 minutes @ 155ºC ≥25MPa
Application Temperature  30ºC - 40ºC


How to use:
1, Part surface should be no oil, dust and impurity
2, Apply the adhesive on parts according to technological requirements. Adhesive thinnest part should be over 1mm. Control the air pressure at 0.4-0.8 Mpa when using pneumatic gun.
3, Heat cure. At 160-190ºC for 30 minutes, the adhesive will full cure.


Packing:
310ml/tube, net weight 460g/tube
 

 

Adhesive